Anti Glare Screen Protector

Our AG screen protector utilizes principle of scattering light through a micro-rough surface, diffusing direct light in different directions. This technique significantly reduces specular reflection of ambient light on tablet screen, effectively minimizing glaring reflections and improving screen readability in outdoor or bright light conditions. At the same time, matte surface effectively reduces adhesion of fingerprints and oil stains. Anti glare screen protector is suitable for outdoor work scenarios such as construction, logistics, inspection, medical and other application environments.

We currently have 3 AR screen protector process options:

Spray/Coating Method: Low cost, simple process, but inconsistent performance.

Chemical Etching Method: Good hand feel, clear and eye-friendly, coating never peels off.

Coating/Magnetron Sputtering Method: Stable structure, long-lasting anti-glare, good wear resistance, high cost.

Share To:

Tablet Anti Glare Screen Protector Specification

Product		2.5D Mate Tablet Tempered Glass
Materials	Glass	0.33mm High Alu Glass
	AB Glue Thickness （120um)	OCA 40um
		PET 50um
		Silicone 30um
	Fingerprint Oil	Electroplating
	Procduct Specs		Electroplating layer <— 0.33mm High Alu Glass layer <— 0.115mm Clear AB Glue layer <— 0.05mm Pet layer
Processing	Thickness	Glass: 0.33mm
		Product: 0.45mm ±0.02
	Edge	Edge≥10c
	Transmittance	≥83%
	Surface Roughness	0.095-0.13um
	Haze level	≦40%
	Hardness	9H
	Surface glossiness	≦50Gu
	Tempered Time	4 Hours

Testing Items		Standard
Performance test	Sticking Testing	The Dimensions match precisely,with no signficant obsrucion to the viewing window or inferference with the normal function of all sensing holes
		Excellent exhaust performance, strong adsorption capacity, and bubble-free operation
		The edge is not irritating to the skin
		Seamless
	Touch sensitivity	No issues affecting touch functionality
	Transmittance testing	≧92%
	Resilience Testing	Bend 90 degrees，no broken
	Drop Testing	Drop： 64G/60CM drop ing 3 times，no broken
	Edge pressure testing	10kg above
	Hardness testing	9H
	Water Angle Testing	Testing 3000 times ≥105 ° ±2
	Temperature Testing	After exposure to temperatures of 80℃ (high) and 40℃ (low) for a continuous period of 48 hours, no bubbles